General grades
The oxygen barrier properties of Soarnol depend on ethylene content and humidity.
The most suitable grade can be determined
according to application and manufacturing process.
|
|
 |
|
|
D2908 |
DT2903 |
DC3212 |
DC3203 |
E3808 |
ET3803 |
A4412 |
AT4406 |
AT4403 |
| Ethylene
content |
|
mol % |
|
29 |
. |
32 |
. |
38 |
. |
44 |
. |
| Density |
|
g/cm3 |
|
1.21 |
|
1.19 |
|
1.17 |
|
1.14 |
|
| Melting
point *1 |
|
C |
. |
1.88 |
. |
183 |
. |
173 |
. |
164 |
. |
| Crystallization
temp. *1 |
|
C |
|
1.63 |
|
160 |
|
152 |
|
144 |
|
| Glass
transition temp. *1 |
|
C |
|
62 |
|
61 |
|
58 |
|
55 |
|
| MFR*2 |
|
g/10 min |
8 |
3.2 |
12 |
3.2 |
8 |
3.2 |
12 |
6 |
3.5 |
|
Apparent melt viscosity *3 |
|
2100 C
poise
Pa s
2300
C
poise
Pa s |
9000
900
5000
500 |
24000
2400
13000
1300 |
5500
550
2500
250 |
24000
2400
13000
1300 |
9000
900
5000
500 |
24000
2400
12000
1200 |
5500
550
2500
250 |
11000
1100
5500
550 |
20000
2000
10000
1000 |
| QTR
*4 |
|
cc
20µ/m2 day atm
cm3
20µ/m2 24hrs MPa |
|
0.4
4 |
|
0.5
5 |
|
0.7
7 |
|
1.5
15 |
|
|
|
blown
film |
|
|
|
|
|
|
|
|
|
| . |
|
Cast
film |
|
|
|
|
|
|
|
|
|
| Manufacturing
process |
|
Sheet |
|
|
|
|
. |
|
. |
. |
|
|
. |
|
Bottle |
|
|
|
|
|
|
. |
. |
. |
|
. |
|
Pipe |
|
. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
*1 Measured by DSC. *2
2100
C, 21, 168N {2160gf} *3 Measured by melt flowtester
with 1mmox10mmL nozzle and 490N{50kgf} load.
*4 200Cx65% RH The data in the
table are our internal standards and not guaranteed figures.
|